Description

The aim of this book is to measure the flow characteristics of blast furnace slag. The industrial slag, synthetically prepared in the laboratory by pure oxides as obtained from market and iron bearing materials with various extents of reduction resembling that expected to be in the cohesive zone as per literature are chosen for measurement while the final slag obtained from the industry reveals shortness of the slag. At C/S ratio of 1.04 to 1.09 and 10.4 to 11.01 MgO % the synthetic slag does not shown a clear trained, the iron bearing materials reveals variation of the characteristics temperature with variation in the extend of the reduction, SEM micrograph and XRD plots of the iron bearing material with different extended of reduction reveal compositional changes associated with structural changes.